Uʻamea filogia maneta Malulu : o se ituaiga uʻamea filogia ma maualuga permeability ma maualalo coercivity i se vaivai maneta fanua. Lenei ituaiga o uʻamea filogia o loʻo faʻaaogaina tele i le leitio eletise alamanuia, meafaigaluega lelei, faʻamamao mamao ma otometi faʻatonutonu faiga. Faʻatasi, e masani ona faʻaaogaina i itu e lua: malosiaga faʻaliliuina ma faʻamatalaga faʻagasologa. O se mea taua i le atunuʻu tamaoaiga.
Uʻamea filogia maneta Fe-Ni vaivai
Vasega: 1J50 (Permalloy), 1J79 (Mumetal, HY-MU80), 1J85 (Supermalloy), 1J46
Tulaga faatonuina: GBn 198-1988
Talosaga: O le tele o tamaʻi fesuiaʻiga, pulupulu fesuiaʻi, moligafua, fesuiaʻiga, maneta mea faʻateleina, uʻamea eletise, koka o loʻo faʻaaogaina mo vaivai ma feololo maneta fanua Flow mama autu ma maneta talipupuni.
|
Faʻavasega |
Vasega |
Tuufaatasiga |
Vasega Tutusa Faava o Malo |
|||
|
IEC |
Lusia |
ISA |
Peretania |
|||
|
Maualuga permeability muamua o uʻamea filogia maneta uʻamea filogia |
1J79 |
Ni79Mo4 |
E11c |
79FO |
Permalloy 80 HY-MU80 |
Mumetal |
|
1J85 |
Ni80Mo5 |
E11c |
79FO |
Supermalloy |
- |
|
|
Maualuga avega uʻamea maualuga maualuga faʻatumuina maneta flux density vaivai uʻamea filogia maneta |
1J46 |
Ni46 |
E11e |
46Н |
45-Permalloy |
|
|
1J50 |
Ni50 |
E11a |
50Н |
Hy-Ra49 |
Radiometal |
|
Vailaʻau o Fe-Ni Soft Alloy Magnetic
|
Vasega |
Vaega o vailaʻau (%) |
||||||||
|
|
C |
P |
S |
Mn |
Si |
Ni |
Mo |
Cu |
Fe |
|
1J46 |
≤0.03 |
≤0.02 |
≤0.02 |
0.6-1.1 |
0.15-0.30 |
45-46.5 |
- |
≤ 0.2 |
Bal |
|
1J50 |
≤0.03 |
≤0.02 |
≤0.02 |
0.3-0.6 |
0.15-0.30 |
49-50.5 |
- |
≤ 0.2 |
Bal |
|
1J79 |
≤0.03 |
≤0.02 |
≤0.02 |
0.6-1.1 |
0.30-0.50 |
78.5 -81.5 |
3.8- 4.1 |
≤ 0.2 |
Bal |
|
1J85 |
≤0.03 |
≤0.02 |
≤0.02 |
0.3-0.6 |
0.15- 0.30 |
79-81 |
4.8- 5.2 |
≤ 0.2 |
Bal |
Meatotino masini:
|
Vasega |
Toe maua mai |
Desinty (g / cm3) |
Curie Point |
Brinellhardness |
σbTensile |
Galue Malosi |
Faʻa umi |
||||
|
Lē faʻailoaina |
|||||||||||
|
1J46 |
0.45 |
8.2 |
400 |
170 |
130 |
735 |
|
735 |
|
3 |
|
|
1J50 |
0.45 |
8.2 |
500 |
170 |
130 |
785 |
450 |
685 |
150 |
3 |
37 |
|
1J79 |
0.55 |
8.6 |
450 |
210 |
120 |
1030 |
560 |
980 |
150 |
3 |
50 |
|
1J85 |
0.56 |
8.75 |
400 |
- |
- |
- |
- |
- |
- |
- |
- |
Maualuga faatumuina maneta induction vaivai uʻamea filogia maneta
Vasega: 1J22 (Hiperco 50)
Tulaga faatonuina: GB / T15002-94
Talosaga: Electromagnet Ji ulu, telefoni samasama diaphragm, torque afi rotor.
| Lusia | ISA | Peretania | Falani | Janpane |
| 50KΦ | Supermendur Hiperco 50 |
Permendur | AFK502 | SME SMEV |
Oloa o vailaʻau:
| C | Mn | Si | P | S | Cu | Ni | Co | V | Fe |
| MAX（≤） | |||||||||
| 0.025 | 0.15 | 0.15 | 0.015 | 0.010 | 0.15 | 0.25 | 47.5-49.5 | 1.75-2.10 | BAL |
Meatotino masini:
| Denstiy （Kg / m3） （g / cm3） |
Toe maua mai （μΩ • mm）（μΩ • cm） |
Curie Poin（℃） | Maneta coefficient （10-6） | Faʻamau maneta （T（KG） | Elastic Modulus （GPa / psi） |
Thermal Conductivity （W / m · K）/ cm · s ℃ |
| 8 120 （8.12） | 400（40） | 940 | 60 | 2.38（23.8） | 207（x103） | 29.8（0.0712） |
Coefficient o Linear Faalauteleina/（10-6/ ° C）
| 20-100 ℃ | 20-200 ℃ | 20-300 ℃ | 20-400 ℃ | 20-500 ℃ | 20-600 ℃ | 20-700 ℃ | 20-800 ℃ |
| 9.2 | 9.5 | 9.8 | 10.1 | 10.4 | 10.5 | 10.8 | 11.3 |
Faia o maneta
| Fomu | Tulaga /（mm / totonu） | Maualalo flx density / mo le mulimuli maneta fanua malosiʻagaT（KG） | |||
| 800 A / m 10Oe |
1.6KA / m 20Oe |
4KA / m 50Oe |
8KA / m 100Oe |
||
| Laupapa | 2.00（20.0） | 2.1（21.0） | 2.20（22.0） | 2.25（22.5） | |
| Pa | 12.7-25.4（0.500-1） | 1.60（16.0） | 1.80（18.0） | 2.00（20.0） | 2.15（21.5） |
| Rod | > 12.7（1） | 1.50（15.0） | 1.75（17.5） | 1.95（19.5） | 2.15（21.5） |