Refractaloy 26 o Fe - NI - Co - Cr faʻafanua faʻamalosi ituaiga deformation o maualuga vevela uʻamea filogia, umi-faʻaaogaina o C - 570 ℃ vevela laina o 540 ℃, o le maualuga vevela mafai ona oʻo i le 677 C, faʻaopopo elemeni o le Cr, mo uʻamea filogia mausali fofo faʻamalosia, maualuga i le maualalo titanium, alumini fiva y matua faʻamalosia vaega, ao viliina elemene faia o titanium, alumini solubility i le mautu fofo ua faʻaititia, uunaia y vaega faʻatapulaʻa aofaʻi faʻateleina, ina ia faʻaleleia atili le vevela mautu o y, faʻaititia y 'vaega o le faʻaputuina malosiaga masei.
O le tuʻufaʻatasia meatotino o le uʻamea filogia e sili atu, ma sili lelei teteʻe teteʻe, malosi malolo ma tolotolo teteʻeina, leai notch maaleale.
Uʻamea filogia |
% |
Ni |
Cr |
Fe |
Mo |
P |
Co |
C |
Mn |
Si |
S |
B |
Al |
Ti |
Faʻaletonu 26 |
Min. |
35.0 |
16.0 |
pulu |
2.5 |
- | 18.0 | - | - | - | - | 0.001 | - | 2.5 |
Max. |
39.0 | 20.0 | 3.5 | 0.03 | 22.0 | 0.08 | 1.0 | 1.5 | 0.03 | 0.01 | 0.25 | 3.0 |
Density
|
8.2 g / cm³
|
Faaliusuavai
|
1200 ℃
|
Tulaga
|
Malosi malosi
Rm N / mm² |
Galue malosi
Rp 0. 2N / mm² |
Faʻa umi
Pei o% |
Brinell maaa
HB
|
Fofo + Matua
|
1000
|
550
|
20
|
331-262
(26-35.5)
|
O le uʻamea filogia na faʻaaogaina i le gaosiaina o laufanua turbine pupuni fale, i lalo o le ausa tulaga o 540 ℃ ~ 570 ℃ mafai ona galue mo le sili atu 100,000 itula, o le faʻaaogaina tulaga e lelei. Tutusa alloys faʻaaogaina i fafo e faia aero tupine afi lavelave vaega O le uʻamea filogia o loʻo i ai ni palasitika lelei i le vevela o le vevela, lea e mafai ona faʻaititia ai le gagauina o vaega ona o le anagata ma tolotolo i le faʻaaoga umi. vevela tele