Incoloy Alloy 800 o se mea faʻaogaina lautele mo meafaigaluega e tatau ona i ai le malosi maualuga ma tetee atu i le faʻamaʻiina, carburizing ma isi aʻafiaga leaga o le maualuga o le vevela (mo faʻaoga maualuga o le vevela e manaʻomia ai le fetolofi ma mea gau, faʻaaoga le Incoloy Alloy 800H ma le 800HT).
Alloy | % | Ni | Cr | Fe | C | Mn | Si | Cu | S | Al | Ti | Al+Ti |
Itupe 800 | Min. | 30 | 19 | paleni | - | - | - | - | - | 0.15 | 0.15 | 0.3 |
Max. | 35 | 23 | 0.10 | 1.5 | 1 | 0.75 | 0.015 | 0.60 | 0.60 | 1.2 | ||
Ilanu 800H | Min. | 30 | 19 | paleni | 0.05 | - | - | - | - | 0.15 | 0.15 | 0.3 |
Max. | 35 | 23 | 0.10 | 1.5 | 1 | 0.75 | 0.015 | 0.60 | 0.60 | 1.2 | ||
Ilanu 800HT | Min. | 30 | 19 | paleni | 0.06 | - | - | - | - | 0.25 | 0.25 | 0.85 |
Max. | 35 | 23 | 0.10 | 1.5 | 1 | 0.75 | 0.015 | 0.60 | 0.60 | 1.2 |
Malosi (g/cm3) | Liu liusuavai (℃ ) | Fa'aula'i fa'alava (GPa) | Fa'avevela vevela (λ/(W(m• ℃)) | Coefficient fa'alauteleina vevela ( 24 -100°C)(m/m °C) | O le vevela o galuega (°C) |
7.94 | 1357-1385 | 196 | 1.28 | 14.2 | -200 ~ +1,100 |
Alloy | Fomu | Tulaga | Malosi'i Sili ksi (MPa) | Fa'aola malosi ile 0.2% fa'ase'eksi (MPa) | Fa'aumiumi ile 2″poo le 4D, pasene |
800 | Pepa, Papatusi | Fa'amauina | 85 (586) | 40 (276) | 43 |
800 | Pepa, Papatusi Strip, Pa | Fa'amauina | 75 (520)* | 30 (205)* | 30* |
800H | Pepa, Papatusi | SHT | 80 (552) | 35 (241) | 47 |
800H | Pepa, Papatusi Strip, Pa | SHT | 65 (450)* | 25 (170)* | 30* |
Pa/Ai | Uaea | Aveese/Uila | Pepa/Ipu | Paipa/Tupa | Fa'atatau |
ASTM B 408 & SB 408 | ASTM B408, AMS 5766, ISO 9723, ISO 9724, BS 3076NA15, BS 3075NA15, EN 10095, VdTüV 412 & 434, AWS A5.11 ENiCrFe-2, AWS A5.1-3 | ASTM B 409/B 906, ASME SB 409/SB 906, ASME Code Case 1325, 2339 | ASTM B409, AMS 5877, BS 3072NA15, BS 3073NA15, VdTüV 412 & 434, DIN 17460, EN 10028-7, EN 10095 | ASTM B 163/ SB 163 | ASTM B366 |
• Lelei le fa'a'a'amea i le fa'asalalauga vai o le maualuga maualuga o le vevela o le 500℃.
• Lelei fa'amamafa fa'afefete
• Lelei masini
• Malosi fetolofi maualuga
• Lelei tele le tete'e i oxidation
• Lelei le tetee atu i kasa mu
• Lelei tele le tetee i carburization
• Lelei le tete'e i le fa'asa'oina o le nitrogen
• Lelei le mautu o le fausaga ile vevela maualuga
• Lelei lelei uelo
• Omea e tineia ai le ogaumu Ethylene• Ta'e le kaponi
• Valve, mea fa'apipi'i ma isi vaega o lo'o fa'aalia i osofa'iga leaga mai le 1100-1800° F
• Ogaumu tau pisinisi• Mea faigaluega fa'avela
• Fa'agaoioiga vaila'au ma petrochemical • Fa'afesuia'i vevela
• Super-vevela ma toe fa'avevela i fale eletise • Va'a mamafa