Hastelloyc C-4 o se austenitic low carbon nickel-molybdenum chromium uʻamea filogia.
O le eseesega autu i le va HastelloyC-4 ma isi vave amata alloys o tutusa vailaʻau tuufaatasiga o le maualalo carbon, ferrosilicate, ma tungsten mea.
O ia vailaʻau tuʻufaʻatasiga faia e faʻaalia lelei sili mautu i 650-1040 ℃, faʻaleleia le agavaʻa e teteʻe ai intergranular 'eleʻele, i lalo o le talafeagai gaosi tulaga mafai ona' aloese mai laina laina pala faʻamamaina ma weld vevela afaina afaina sone.
Uʻamea filogia |
% |
Fe |
Cr |
Ni |
Mo |
Co |
C |
Mn |
Si |
S |
P |
W |
V |
Hastelloy C-4 |
Min. |
- |
14.0 |
paleni |
14.0 | - | - | - | - | - | - |
2.5 |
- |
Max. |
3.0 |
18.0 |
17.0 |
2.0 | 0.015 | 3.0 | 0.1 | 0.01 | 0.03 | 3.5 | 0.2 |
Density
|
8.94 g / cm³
|
Faaliusuavai
|
1325-1370 ℃
|
Tulaga
|
Malosi malosi
Rm N / mm² |
Galue malosi
Rp 0. 2N / mm² |
Faʻa umi
Pei o% |
Brinell maaa
HB
|
Fofo togafitiga
|
690
|
276
|
40
|
-
|
Pa / Rod | Fasimea / Coil | Pepa / Papatusi | Paipa / Faagaau | Faamagaloga |
ASTM B335 | ASTM B333 | ASTM B622, ASTM B619, ASTM B626 | ASTM B564 |
• Lelei tele o le pala i le tele o mea leaga faʻasalalau, aemaise i le faʻaititia o tulaga.
• Lelei tele i le lotoifale 'eleʻele tetee i halides.
• Fuafua kesi desulfurization kasa
• Pikoina ma acid toe faʻafouina laʻau
• Acetic acid ma le faʻatupuina o vailaʻau oona
• Gaosiga o le Titanium dioxide (metotia o le chlorine)
• Eletise