Haynes® 25 (L-605) o se kesi faʻavae uʻamea filogia e tuʻufaʻatasia lelei fausiaina ma sili atu maualuga vevela meatotino. O le uʻamea filogia e tetee i le oxidation ma carburization i le 1900 ° F. Uʻamea filogia 25 mafai ona faʻamaʻaʻaina tele e galue malulu. Malulu galue o le a faʻateleina tolotolo malosi e oʻo atu i le 1800 ° F ma le faʻaletonu loto vaivai uo i le 1500 ° F. Faʻamaʻa matutua i le 700 - 1100 ° F faʻalelei atili tolotolo ma faʻateʻa mamafa faʻamamaina malosiaga i lalo ole 1300 ° F.
Uʻamea filogia |
% |
Ni |
Cr |
Co |
Mn |
Fe |
C |
Si |
S |
P |
W |
Haynes 25 |
Min. |
9.0 |
19.0 |
paleni |
1.0 | - | 0.05 | - | - | - |
14.0 |
Max. |
11.0 |
21.0 | 2.0 | 3.0 | 0.15 | 0.4 | 0.03 | 0.04 | 16.0 |
Density
|
9.13 g / cm³
|
Faaliusuavai
|
1330-1410 ℃
|
Tulaga
|
Malosi malosi
Rm N / mm² |
Galue malosi
Rp 0. 2N / mm² |
Faʻa umi
Pei o% |
Brinell maaa
HB
|
Fofo togafitiga
|
960
|
340
|
35
|
≤282
|
AMS5759, AMS5537, ASTM F90, AMS 5796
Pa / Rod | Faamagaloga | Fasimea / Coil | Pepa / Papatusi | Paipa / Faagaau |
AMS5759, ASTM F90 | AMS 5759 | AMS5537 | AMS5537 | GE B50T26A |
1. Tumau feololo ma tolotolo malosi i lalo ole 815.
2. Lelei sili atu le faʻamamaina o le oxidation i lalo ole 1090 '
3. Faʻamalieina fausiaina, uelo ma isi tekonolosi meatotino.
Haynes 25 ua tuuina atu auaunaga lelei i le tele o vaalele afi vaega. O ni isi o ia mea e aofia ai lauʻau pipi, potu faʻamuina, vaega mulimuli o le afi, ma mama tupine. O le uʻamea filogia na faʻaaogaina foʻi ma le manuia i le tele o ituaiga ogaumu ogaumu apalai e aofia ai muffles ogaumu ma ie e ufiufi ai i nofoaga ogaoga i ogaumu vevela.