Alloy31 o se tasi ituaiga o azotic finau uʻamea nichrome molybdenum uʻamea filogia, o le faʻatinoga o loʻo tu i le va o le maoaʻe austenite uʻamea stainless ma le nickel base uʻamea filogia, O le i ai o le 'apamemea faʻateleina lona teteʻe atu i sulfuric acid. O le uʻamea filogia o loʻo faʻaaogaina i le vailaʻau ma le petrochemical gaosi alamanuia. Uʻamea filogia tubes malulu galulue i maualuga maualuga tulaga mo downhole auaunaga i moderately paʻu loloto loloto loloto kesi kesi.
Uʻamea filogia |
% |
Ni |
Cr |
Fe |
Mo |
N |
C |
Mn |
Si |
S |
Cu |
P |
Uʻamea filogia31 |
Min. |
30.0 |
26.0 |
Bal |
6.0 |
0.15 |
|
|
|
|
1.0 |
|
Max. |
32.0 |
28.0 |
7.0 |
0.2 |
0.015 |
2.0 |
0.3 |
0.01 |
1.4 |
0.02 |
Density
|
8.10 g / cm³
|
Faaliusuavai
|
1350-1370 ℃
|
Tulaga
|
Malosi malosi
Rm N / mm² |
Galue malosi
Rp 0. 2N / mm² |
Faʻa umi
Pei o% |
Brinell maaa
HB
|
Fofo togafitiga
|
650
|
350
|
35
|
≤363
|
ASTM B 668, B709, B 829, ASME SB-668, SB-709, SB-829
Alloy31 o se tasi ituaiga o azotic finau uʻamea filogia molybdenum uʻamea filogia, o le gaioiga o loʻo tu i le va o le maoaʻe austenite uʻamea stainless ma le limasene faavae uʻamea filogia
1. galue
2.High malosi malosi, tumau tumau, tolotolo malosi ma vaeluaina le malosi i le 700.
3.High inoima gafatia at1000 ℃.
4.Steady masini faʻatinoina i le maualalo o le vevela.
Alloy 31 suti faʻaaogaina i le kemisi ma le suauʻu vailaʻau vailaʻau alamanuia, le siosiomaga poloketi ma le suauʻu, kesi, ma isi luga o pisinisi matata ..