MP35N o se non-maneta nickel ma cobalt chromium molybdenum uʻamea filogia. Maualuga malosi maluluina, oo atu i le 300ksi [2068MPa]) lelei ductility maaa Ma corrosion tetee sili tetee tetee i vulcanization, maualuga vevela oxidation ma le faatinoga o le hydrogen opoopoina. O le tulaga ese gaioiga e ala i le galue faʻamaʻaʻaina, vaega suiga ma tuai togafitiga. Afai e faʻaaogaina i lalo o le tuutuuga o le galue atoa faʻamaʻaina, o le vevela o le faʻagaioiga o le -200~315°C, ma le maualuga maualuga fautuaina vevela o 750 tikeri Fahrenheit (399 tikeri c)
C |
Mn |
P |
S |
Si |
Cr |
Ni |
Mo |
Co |
Ti |
B |
Te |
≦ 0.03 |
≦ 0.15 |
≦ 0.015 |
≦ 0.010 |
≦ 0.15 |
19.0 21.0 |
33.0 37.0 |
9.0 10.50 |
≧ 35.0 |
≦ 1.0 |
≦ 0.01 |
≦ 1.0 |
Density (G / cm3) |
Faaliusuavai (° C) |
Faalauteleina coefficient (M / (m · ° C) (21-93 ° C)) |
8.43 | 1440 | 12.8 × 10E-6 |
Tulaga | σb Faasao |
σ0.2 Faasao |
φ % |
Ψ % |
Faigata HRC |
Fofo mautu + Malulu galue |
1758 | 1551 | 12 | 50 | 45 |
Fofo mautu + Malulu galue + Matua |
1792 | 1585 | 8 | 35 | 38min |
AMS5758 、 AMS5844 、 AMS5845 、 ANSI / ASTM F56
• Lelei tetee atu i Vulcanization, maualuga vevela oxidation, crisp, masima puao ma le tele o minerale acid.
• Lelei tetee atu i le popolevale corrosion taʻe i le faigata siosiomaga ma maualuga malosi.
• Maualuga le teteʻe ile faʻafanua eletise, pei ole paina o le pala ma le tafe o le vai.
MP35N uʻamea filogia mafai ona faʻaaogaina mo togafitiga faʻafomaʻi, vai sami, suauʻu ma kesi Wells, kemisi ma faʻapipiʻi, tautotogo,
Maneta vaega ma mea faigaluega vaega o le siʻosiʻomaga o meaai gaosi