♦ Ueloina Igoa Mea: Nika maopoopo uaea, ErNiCrMo-4, Hastelloy C276 Maea uaea
♦ MOQ: 15kg
♦ Fomu: MIG (15kgs / spool), TIG (5kgs / pusa)
♦ Tele: lapoa 0.01mm-8.0mm
♦ Lautele Lautele: 0.8MM / 1.0MM / 1.2MM / 1.6MM / 2.4MM / 3.2MM / 3.8MM / 4.0MM / 5.0MM
♦ Tulaga Faatonuina: E tusa ma Tusipasi AWS A5.14 ASME SFA A5.14
ErNiCrMo-4 o loʻo faʻaaogaina mo le faʻamamaina Hastelloy C276, Nickel base uʻamea filogia ma isi mea, Nickel uʻamea filogia i uʻamea poʻo le sila uʻamea, faʻaaogaina foi mo uelo Nickel CrMo uʻamea filogia tuʻufaʻatasia vaega luga uʻamea. Mauga uʻamea mea o tutusa tuʻufaʻatasi vailaʻau faʻapea foi ma dissimilar mea o nickel faʻavae alloys , uʻamea ma uʻamea stainless. Lenei uʻamea filogia mafai foi ona faʻaaogaina mo cladding uʻamea ma nickel-chrome-molybdenum uʻamea uamea. Ole maualuga ole molybdenum mataupu e maua ai le teteʻe tele ile faʻamamaina ole pala, taina ma pupuʻu palapala.
C |
Cr |
Ni |
Si |
Mn |
P |
S |
Cu |
Fe |
V |
W |
Mo |
Co |
≤0.02 |
14.5-16.5 |
Pa | ≤0.08 | ≤1.0 | ≤0.04 | ≤0.03 | ≤0.5 | 4.0-7.0 |
≤0.35 |
3.0-4.0 | 15.0-17.0 | ≤2.5 |
Lapoa | Faʻagasologa | Volt | Amps | Puipuia Kasa | |
I totonu | mm | ||||
0.035 | 0.9 | GMAW | 26-29 | 150-190 | Faʻafefe Transfer100% Argon |
0.045 | 1.2 | GMAW | 28-32 | 180-220 | |
1/16 | 1.6 | GMAW | 29-33 | 200-250 | |
1/16 | 1.6 | GMAW | 14-18 | 90-130 | 100% Argon |
3/32 | 2.4 | GMAW | 15-20 | 120-175 | 100% Argon |
1/8 | 3.2 | GMAW | 15-20 | 150-220 | 100% Argon |
Tulaga | Tensile Malosi MPa (ksi) | Galue Malosi MPa (ksi) | Elongation% |
AWS toe faʻaleleia | 690 (100) | Le faʻamaotiina | Le faʻamaotiina |
Iuga masani e pei ona uʻamea | 730 (106) | 540 (79) | 39 |
MIG : 75% Ar / 25% Ia
TIG : 100% Ar
O le uʻamea filogia o lo o tetee atu i acid ma asu ausa otaota. Ona o lona maualuga molybdenum anotusi, o loo i ai le malosi tetee atu i popole popolevale pala, pitting ma cavitation palapala
Lautele faʻaaogaina i vailaʻau koneteina pipelines, pamu afuala, mana alamanuia flue kesi desulfurization ma uelo -196, talosaga o 9% Ni uʻamea.