3J01 uʻamea filogia o se Fe-Ni-Cr austenite faʻamaluluina uʻamea faʻamalosia maualuga uʻamea filogia filogia.After mautu fofo togafitiga, e lelei plasticity, maualalo maaa ma faigofie gaioiga ma fausiaina. Maualuga masini ma ofuvae eletise na maua ina ua maeʻa fofo malulu poʻo malulu faʻamaʻi matutua togafitiga.
Uʻamea filogia | C | Mn | Si | P | S | Ni | Cr | Ti | Al | Fe |
3J01 | ≤0.05 | ≤1.00 | ≤0.80 | ≤0.020 | ≤0.020 | 34.5-36.5 | 11.5-13.0 | 2.70-3.20 | 1.00-1.80 | Faasa |
Density
(g / cm3)
|
Teteeina (L2 - m) |
Vickers
maaʻa
(HV)
|
Modulus o ofuvae(E / MPa) | Shear deformation(G / MPa) | Malosiaga taimi(K / 106) |
8.0
|
1.02
|
400-480 | 186500-206000 | 68500-78500 | 150-250 |
Tulaga | Mafiafia / lapoa (mm) | Malosi malosi σb / MPa | Faʻa umi Pei o% |
faapipiiina | 0.20 ~ 0.50 | ≤981 | ≥20 |
Malulu tusia | 0.20 ~ 3.0 | ≥981 | - |
3J01 uʻamea filogia o loʻo i ai uiga o le maualuga malosi, maualuga eletise modulus, laʻititi eletise mulimuli aneffect ma hysteresis, vaivai magnetism, lelei oona tetee ma faʻamautuina vevela, ma mafai ona galue i lalo o maualuga maualuga vevela, sili atu faʻafitauli poʻo faigata auala faʻasalalau.
Faʻaaoga e gaosia ai ituaiga uma o eletise eletise elemene maaleale vaega ma vaega e teteʻe atu i le nitric acid poʻo isi auala faʻapolopolo ala o faʻasalalauga, e pei o ata tifaga, diaphragms, faʻafefe, faʻaliliu uʻamea, faʻafefe ma isi ofuvae eletise.