♦ Weliding Igoa uaea: ErNiCrMo-3, Inconel 625 TIG / MIG uaea
♦ MOQ:15kg
♦ Fomu: MIG (15kgs / atigivae), TIG (5kgs / pusa)
♦ tele: Lapoa 0.01mm-8.0mm
♦ Lautele Lautele:0.8MM / 1.0MM / 1.2MM / 1.6MM / 2.4MM / 3.2MM / 3.8MM / 4.0MM / 5.0MM
♦ Tulaga Faatonuina: O gatasi ma Tusipasi AWS A5.14 ASME SFA A5.14
ErNiCrMo-3 faaaogaina mo ueloina 625 (N06625) uʻamea filogia, 20 uʻamea filogia, 825,25-6Mo, 9% Ni uamea po o isi molybdenum uamea, na faʻaaogaina foi mo ueloina o mea eseese ma 'eleʻele tetee luga o mea mea i luga.
Lelei tele meatotino masini i maualuga ma maualalo vevela. Tetee atu i le malosi o le pala, faʻafitauli oona oona, pitting ma backlash palapala i le tele o ituaiga o oxidation ma faʻaititia faʻasalalauga.
C |
Al |
Si |
Mn |
Cr |
Ni |
Ti |
Fe |
S |
Cu |
Mo |
P |
Nb + Ta |
Isi |
≤0.10 |
≤0.40 |
≤0.50 |
≤0.50 |
20.0 - 23.0 |
≥58.0 |
≤0.40 |
≤5.0 |
≤0.015 |
≤0.50 |
8.0 - 10.0 |
≤0.02 |
3.15 - 4.15 |
≤0.50 |
Lapoa | Faʻagasologa | Volt | Amps | Puipuia Kasa | |
I totonu | mm | ||||
0.035 | 0.9 | GMAW | 26-29 | 150-190 | Faʻafefe Transfer100% Argon |
0.045 | 1.2 | 28-32 | 180-220 | ||
1/16 | 1.6 | 29-33 | 200-250 | ||
1/16 | 1.6 | GTAW | 14-18 | 90-130 | 100% Argon |
3/32 | 2.4 | 15-20 | 120-175 | ||
1/8 | 3.2 | 15-20 | 150-220 |
Tulaga | Tensile Malosi MPa (ksi) | Galue Malosi MPa (ksi) | Elongation% |
AWS toe faʻaleleia | 760 (110) | Le faʻamaotiina | Le faʻamaotiina |
Iuga masani e pei ona uʻamea | 790 (115) | 590 (85) | 35 |
Maualuga uʻamea mea, e mafai ona faʻaaogaina i le faʻaopoopoina o nickel-chromium molybdenum uʻamea filogia,
E mafai ona faʻaaogaina mo le faʻaaogaina o ofu ma uʻamea o uʻamea eseese e pei o Ni-Cr-Mo uʻamea filogia ma uʻamea stainless ma carbon carbon
E i ai le lelei oxidation tetee ma faʻaititia le siosiomaga.
O le maualuga mea i totonu o molybdenum maua lelei popolega ma teteʻe atu i pitting ma vaeluaina palapala.
ERNiCrMo-3 Talosaga fanua :
E talafeagai mo le ueloina o nickel-chrome-molybdenum uʻamea filogia, e pei o Inconel625, Incoy 825, ma e mafai foi ona faʻaaogaina mo le ueloina ma le fauina o le nickel-base alloy ma le stainless steel dissimilar mea. E mafai ona faʻaaogaina i le siosiomaga mai le maualalo o le vevela i le 540 ℃.