NIMONIC® uʻamea filogia 75 o se 80/20 nickel-chromium uʻamea filogia ma faʻatonutonuina faʻaopopoga o titanium ma carbon. Muamua faʻalauiloaina i le 1940s mo turbine blades i le prototype Faʻavae afi vaʻalele, ua tele nei ona faʻaaoga mo pepa apalai valaʻau mo le faʻamamaina o le oxidation ma scaling teteʻe faʻatasi ai ma le malosi feololo i le maualuga faʻagaioiga vevela. O loʻo faʻaaogaina pea ile kesi kesi afi faʻapisinisi faʻapea foi ma le gaosiaina o mea vevela tau alamanuia, ogaumu ogaumu ma meafaigaluega vevela-togafitiga. E faigofie ona fausiaina ma ueloina
Uʻamea filogia |
% |
Ni |
Cr |
Fe |
Co |
C |
Mn |
Si |
Ti |
Nimonic 75 |
Min. |
Paleni |
18.0 | - | - | 0.08 | - | - |
0.2 |
Max. |
21.0 | 5.0 | 0.5 | 0.15 | 1.0 | 1.0 |
0.6 |
Density
|
8.37 g / cm³
|
Faaliusuavai
|
1340-1380 ℃
|
Tulaga
|
Malosi malosi
Rm (faʻasuafaina (Faasao) |
Galue malosi
Ne faʻasologa (Faasao) |
Faʻa umi
Pei o% |
Modulus eletise
(GPa) |
Fofo togafitiga
|
750
|
275 | 42 | 206 |
Pa / Rod | Uaea | Fasimea / Coil | Pepa / Papatusi | Paipa / Faagaau |
BSHR 5, BS HR 504, DIN 17752, AECMA
PrEN2306, AECMA PrEN2307, AECMA
PrEN2402, ISO 9723-25
|
O BS HR 203, DIN
17750, AECMA PrEN2293, AECMA
PrEN2302, AECMA PrEN2411, ISO 6208
|
O BS HR 403, DIN 17751,
AECMA PrEN2294, ISO 6207
|
• Lelei weldability
• Lelei gaioiga
• Tetee pala lelei
• Lelei masini meatotino
• Tetee vevela maualuga lelei
• Faʻamau vaʻalele
• Inisinia afi afi
• Vaega fausaga o ogaumu ogaumu
• Vevela togafitiga masini
• Inisinia faaniukilia